Wafer producing method

ABSTRACT

A wafer producing method for producing a hexagonal single crystal wafer from a hexagonal single crystal ingot is disclosed. The wafer producing method includes a separation start point forming step of forming a modified layer parallel to the upper surface of the ingot and cracks extending from the modified layer to thereby form a separation start point in the ingot. The separation start point forming step includes a first separation start point forming step of setting the focal point of a laser beam at a first depth which is N times (N is an integer not less than 2) the depth corresponding to the thickness of the wafer from the upper surface of the ingot and next applying the laser beam to the ingot to thereby form a first separation start point composed of a first modified layer and first cracks extending therefrom.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a wafer producing method for slicing a hexagonal single crystal ingot to produce a wafer.

2. Description of the Related Art

Various devices such as ICs and LSIs are formed by forming a functional layer on the front side of a wafer formed of silicon or the like and partitioning this functional layer into a plurality of regions along a plurality of crossing division lines. The division lines of the wafer are processed by a processing apparatus such as a cutting apparatus and a laser processing apparatus to thereby divide the wafer into a plurality of individual device chips corresponding to the respective devices. The device chips thus obtained are widely used in various equipment such as mobile phones and personal computers. Further, power devices or optical devices such as LEDs and LDs are formed by forming a functional layer on the front side of a wafer formed of a hexagonal single crystal such as SiC and GaN and partitioning this functional layer into a plurality of regions along a plurality of crossing division lines.

In general, the wafer on which the devices are to be formed is produced by slicing an ingot with a wire saw. Both sides of the wafer obtained above are polished to a mirror finish (see Japanese Patent Laid-open No. 2000-94221, for example). This wire saw is configured in such a manner that a single wire such as a piano wire having a diameter of about 100 to 300 μm is wound around many grooves formed on usually two to four guide rollers to form a plurality of cutting portions spaced in parallel with a given pitch. The wire is operated to run in one direction or opposite directions, thereby slicing the ingot into a plurality of wafers.

However, when the ingot is cut by the wire saw and both sides of each wafer are polished to obtain the product, 70 to 80% of the ingot is discarded to cause a problem of poor economy. In particular, a hexagonal single crystal ingot of SiC or GaN, for example, has high Mohs hardness and it is therefore difficult to cut this ingot with the wire saw. Accordingly, considerable time is required for cutting of the ingot, causing a reduction in productivity. That is, there is a problem in efficiently producing a wafer in this prior art.

A technique for solving this problem is described in Japanese Patent Laid-open No. 2013-49461. This technique includes the steps of setting the focal point of a laser beam having a transmission wavelength to SiC inside a hexagonal single crystal ingot, next applying the laser beam to the ingot as scanning the laser beam on the ingot to thereby form a modified layer and cracks in a separation plane inside the ingot, and next applying an external force to the ingot to thereby break the ingot along the separation plane where the modified layer and the cracks are formed, thus separating a wafer from the ingot. In this technique, the laser beam is scanned spirally or linearly along the separation plane so that a first application point of the laser beam and a second application point of the laser beam nearest to the first application point have a predetermined positional relation with each other. As a result, the modified layer and the cracks are formed at very high density in the separation plane of the ingot.

SUMMARY OF THE INVENTION

However, in the ingot cutting method described in Japanese Patent Laid-open No. 2013-49461 mentioned above, the laser beam is scanned spirally or linearly on the ingot. In the case of linearly scanning the laser beam, the direction of scanning of the laser beam is not specified. In the ingot cutting method described in Japanese Patent Laid-open No. 2013-49461, the pitch (spacing) between the first application point and the second application point of the laser beam as mentioned above is set to 1 to 10 μm. This pitch corresponds to the pitch of the cracks extending from the modified layer along a c-plane defined in the ingot.

In this manner, the pitch of the application points of the laser beam to be applied to the ingot is very small. Accordingly, regardless of whether the laser beam is scanned spirally or linearly, the laser beam must be applied with a very small pitch and the improvement in productivity is not yet sufficient.

It is therefore an object of the present invention to provide a wafer producing method which can efficiently produce a wafer from an ingot.

In accordance with an aspect of the present invention, there is provided a wafer producing method for producing a hexagonal single crystal wafer from a hexagonal single crystal ingot having a first surface, a second surface opposite to the first surface, a c-axis extending from the first surface to the second surface, and a c-plane perpendicular to the c-axis, the wafer producing method including: a separation start point forming step of setting a focal point of a laser beam having a transmission wavelength to the ingot inside the ingot at a predetermined depth from the first surface, which depth corresponds to a thickness of the wafer to be produced, and next applying the laser beam to the first surface as relatively moving the focal point and the ingot to thereby form a modified layer parallel to the first surface and cracks extending from the modified layer along the c-plane, thus forming a separation start point; and a wafer separating step of separating a plate-shaped member having a thickness corresponding to the thickness of the wafer from the ingot at the separation start point after performing the separation start point forming step, thus producing the wafer from ingot. The separation start point forming step includes: a modified layer forming step of relatively moving the focal point of the laser beam in a first direction perpendicular to a second direction where the c-axis is inclined by an off angle with respect to a normal to the first surface and the off angle is formed between the first surface and the c-plane, thereby linearly forming the modified layer extending in the first direction; and an indexing step of relatively moving the focal point in the second direction to thereby index the focal point by a predetermined amount. The modified layer forming step includes: a first separation start point forming step of setting the focal point of the laser beam at a first depth which is N times (N is an integer not less than 2) the depth corresponding to the thickness of the wafer from the first surface of the ingot and next applying the laser beam to the first surface of the ingot to thereby form a first separation start point composed of a first modified layer and first cracks extending therefrom; and a second separation start point forming step of setting the focal point of the laser beam at a second depth obtained by subtracting the depth corresponding to the thickness of the wafer from the first depth of the first separation start point toward the first surface of the ingot and next applying the laser beam to the first surface of the ingot to thereby form a second separation start point composed of a second modified layer and second cracks extending therefrom, after performing the first separation start point forming step.

Preferably, the hexagonal single crystal ingot is selected from an SiC single crystal ingot and a GaN single crystal ingot.

According to the wafer producing method of the present invention, the modified layer forming step includes the first separation start point forming step of setting the focal point of the laser beam at the first depth which is N times (N is an integer not less than 2) the depth corresponding to the thickness of the wafer from the first surface of the ingot and next applying the laser beam to the first surface of the ingot to thereby form the first separation start point at the first depth inside the ingot, and also includes the second separation start point forming step of setting the focal point of the laser beam at the second depth obtained by subtracting the depth corresponding to the thickness of the wafer from the first depth of the first separation start point toward the first surface of the ingot and next applying the laser beam to the first surface of the ingot to thereby form the second separation start point at the second depth inside the ingot. Accordingly, a plate-shaped member having a thickness corresponding to the thickness of the wafer can be first separated from the ingot at the second separation start point, and another plate-shaped member having a thickness corresponding to the thickness of the wafer can be next separated from the ingot at the first separation start point. Thusly, a plurality of hexagonal single crystal wafers can be efficiently produced from the ingot.

Accordingly, the productivity can be sufficiently improved, and the amount of the ingot to be discarded can be sufficiently reduced to about 30%.

The above and other objects, features and advantages of the present invention and the manner of realizing them will become more apparent, and the invention itself will best be understood from a study of the following description and appended claims with reference to the attached drawings showing a preferred embodiment of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a perspective view of a laser processing apparatus suitable for use in performing a wafer producing method of the present invention;

FIG. 2 is a block diagram of a laser beam generating unit;

FIG. 3A is a perspective view of a hexagonal single crystal ingot;

FIG. 3B is an elevational view of the ingot shown in FIG. 3A;

FIG. 4 is a perspective view for illustrating a separation start point forming step;

FIG. 5 is a plan view of the ingot shown in FIG. 3A;

FIG. 6 is a schematic sectional view for illustrating a modified layer forming step;

FIG. 7 is a schematic plan view for illustrating the modified layer forming step;

FIG. 8A is a schematic plan view for illustrating an indexing step;

FIG. 8B is a schematic plan view for illustrating an index amount;

FIGS. 9A and 9B are perspective views for illustrating a wafer separating step;

FIG. 10 is a perspective view of a hexagonal single crystal wafer produced from the ingot; and

FIGS. 11A to 11C are schematic sectional views for illustrating a wafer producing method according to a preferred embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

A preferred embodiment of the present invention will now be described in detail with reference to the drawings. Referring to FIG. 1, there is shown a perspective view of a laser processing apparatus 2 suitable for use in performing a wafer producing method of the present invention. The laser processing apparatus 2 includes a stationary base 4 and a first slide block 6 mounted on the stationary base 4 so as to be movable in the X direction. The first slide block 6 is moved in a feeding direction, or in the X direction along a pair of guide rails 14 by a feeding mechanism 12 composed of a ball screw 8 and a pulse motor 10.

A second slide block 16 is mounted on the first slide block 6 so as to be movable in the Y direction. The second slide block 16 is moved in an indexing direction, or in the Y direction along a pair of guide rails 24 by an indexing mechanism 22 composed of a ball screw 18 and a pulse motor 20. A support table 26 is mounted on the second slide block 16. The support table 26 is movable in the X direction and the Y direction by the feeding mechanism 12 and the indexing mechanism 22 and also rotatable by a motor stored in the second slide block 16.

A column 28 is provided on the stationary base 4 so as to project upward therefrom. A laser beam applying mechanism (laser beam applying means) 30 is mounted on the column 28. The laser beam applying mechanism 30 is composed of a casing 32, a laser beam generating unit 34 (see FIG. 2) stored in the casing 32, and focusing means (laser head) 36 movably mounted in the Z direction on the front end of the casing 32. An imaging unit 38 having a microscope and a camera is also mounted on the front end of the casing 32 so as to be aligned with the focusing means 36 in the X direction.

As shown in FIG. 2, the laser beam generating unit 34 includes a laser oscillator 40 for generating a pulsed laser beam such as YAG laser and YVO4 laser, repetition frequency setting means 42 for setting the repetition frequency of the pulsed laser beam to be generated from the laser oscillator 40, pulse width adjusting means 44 for adjusting the pulse width of the pulsed laser beam to be generated from the laser oscillator 40, and power adjusting means 46 for adjusting the power of the pulsed laser generated from the laser oscillator 40. Although especially not shown, the laser oscillator 40 has a Brewster window, so that the laser beam generated from the laser oscillator 40 is a laser beam of linearly polarized light. After the power of the pulsed laser beam is adjusted to a predetermined power by the power adjusting means 46 of the laser beam generating unit 34, the pulsed laser beam is reflected by a mirror 48 included in the focusing means 36 and next focused by a focusing lens 50 included in the focusing means 36. The focusing lens 50 is positioned so that the pulsed laser beam is focused inside a hexagonal single crystal ingot 11 as a workpiece fixed to the support table 26.

Referring to FIG. 3A, there is shown a perspective view of the hexagonal single crystal ingot 11 as a workpiece to be processed. FIG. 3B is an elevational view of the hexagonal single crystal ingot 11 shown in FIG. 3A. The hexagonal single crystal ingot (which will be hereinafter referred to also simply as ingot) 11 is selected from a SiC single crystal ingot or a GaN single crystal ingot. The ingot 11 has a first surface (upper surface) 11 a and a second surface (lower surface) 11 b opposite to the first surface 11 a. The first surface 11 a of the ingot 11 is preliminarily polished to a mirror finish because the laser beam is applied to the first surface 11 a.

The ingot 11 has a first orientation flat 13 and a second orientation flat 15 perpendicular to the first orientation flat 13. The length of the first orientation flat 13 is set greater than the length of the second orientation flat 15. The ingot 11 has a c-axis 19 inclined by an off angle α toward the second orientation flat 15 with respect to a normal 17 to the upper surface 11 a and also has a c-plane 21 perpendicular to the c-axis 19. The c-plane 21 is inclined by the off angle α with respect to the upper surface 11 a. In general, in the hexagonal single crystal ingot 11, the direction perpendicular to the direction of extension of the shorter second orientation flat 15 is the direction of inclination of the c-axis 19. The c-plane 21 is set in the ingot 11 innumerably at the molecular level of the ingot 11. In this preferred embodiment, the off angle α is set to 4°. However, the off angle α is not limited to 4° in the present invention. For example, the off angle α may be freely set in the range of 1° to 6° in manufacturing the ingot 11.

Referring again to FIG. 1, a column 52 is fixed to the left side of the stationary base 4. The column 52 is formed with a vertically elongated opening 53, and a pressing mechanism 54 is vertically movably mounted to the column 52 so as to project from the opening 53.

As shown in FIG. 4, the ingot 11 is fixed to the upper surface of the support table 26 by using a wax or adhesive in the condition where the second orientation flat 15 of the ingot 11 becomes parallel to the X direction. In other words, as shown in FIG. 5, the direction of formation of the off angle α is shown by an arrow Y1. That is, the direction of the arrow Y1 is the direction where the intersection 19 a between the c-axis 19 and the upper surface 11 a of the ingot 11 is present with respect to the normal 17 to the upper surface 11 a. Further, the direction perpendicular to the direction of the arrow Y1 is shown by an arrow A. Then, the ingot 11 is fixed to the support table 26 in the condition where the direction of the arrow A becomes parallel to the X direction.

Accordingly, the laser beam is scanned in the direction of the arrow A perpendicular to the direction of the arrow Y1, or the direction of formation of the off angle α. In other words, the direction of the arrow A perpendicular to the direction of the arrow Y1 where the off angle α is formed is defined as the feeding direction of the support table 26.

In the wafer producing method of the present invention, it is important that the scanning direction of the laser beam to be applied from the focusing means 36 is set to the direction of the arrow A perpendicular to the direction of the arrow Y1 where the off angle α of the ingot 11 is formed. That is, it was found that by setting the scanning direction of the laser beam to the direction of the arrow A as mentioned above in the wafer producing method of the present invention, cracks propagating from a modified layer formed inside the ingot 11 by the laser beam extend very long along the c-plane 21.

In performing the wafer producing method according to this preferred embodiment, a separation start point forming step is performed in such a manner that the focal point of the laser beam having a transmission wavelength (e.g., 1064 nm) to the hexagonal single crystal ingot 11 fixed to the support table 26 is set inside the ingot 11 at a predetermined depth from the first surface (upper surface) 11 a, which depth corresponds to the thickness of a wafer to be produced, and the laser beam is next applied to the upper surface 11 a as relatively moving the focal point and the ingot 11 to thereby form a modified layer 23 parallel to the upper surface 11 a and cracks 25 propagating from the modified layer 23 along the c-plane 21, thus forming a separation start point (separation plane) where the modified layer 23 and the cracks 25 are formed.

This separation start point forming step includes a modified layer forming step of relatively moving the focal point of the laser beam in the direction of the arrow A perpendicular to the direction of the arrow Y1 where the c-axis 19 is inclined by the off angle α with respect to the normal 17 to the upper surface 11 a and the off angle α is formed between the c-plane 21 and the upper surface 11 a, thereby forming the modified layer 23 inside the ingot 11 and the cracks 25 propagating from the modified layer 23 along the c-plane 21, and also includes an indexing step of relatively moving the focal point in the direction of formation of the off angle α, i.e., in the Y direction to thereby index the focal point by a predetermined amount as shown in FIG. 7 and FIGS. 8A and 8B.

As shown in FIGS. 6 and 7, the modified layer 23 is linearly formed so as to extend in the X direction, so that the cracks 25 propagate from the modified layer 23 in opposite directions along the c-plane 21. In the wafer producing method according to this preferred embodiment, the separation start point forming step further includes an index amount setting step of measuring the width of the cracks 25 formed on one side of the modified layer 23 along the c-plane 21 and then setting the index amount of the focal point according to the width measured above. More specifically, letting W1 denote the width of the cracks 25 formed on one side of the modified layer 23 so as to propagate from the modified layer 23 along the c-plane 21, the index amount W2 of the focal point is set in the range of W1 to 2W1.

For example, the separation start point forming step is performed under the following laser processing conditions.

Light source: Nd:YAG pulsed laser

Wavelength: 1064 nm

Repetition frequency: 80 kHz

Average power: 3.2 W

Pulse width: 4 ns

Spot diameter: 10 μm

Numerical aperture (NA) of the focusing lens: 0.45

Index amount: 400 μm

In the laser processing conditions mentioned above, the width W1 of the cracks 25 propagating from the modified layer 23 along the C-plane 21 in one direction as viewed in FIG. 6 is set to about 250 μm, and the index amount W2 is set to 400 μm. However, the average power of the laser beam is not limited to 3.2 W. When the average power of the laser beam was set to 2 to 4.5 W, good results were obtained in the preferred embodiment. In the case that the average power was set to 2 W, the width W1 of the cracks 25 was about 100 μm. In the case that the average power was set to 4.5 W, the width W1 of the cracks 25 was about 350 μm.

In the case that the average power is less than 2 W or greater than 4.5 W, the modified layer 23 cannot be well formed inside the ingot 11. Accordingly, the average power of the laser beam to be applied is preferably set in the range of 2 to 4.5 W. For example, the average power of the laser beam to be applied to the ingot 11 was set to 3.2 W in this preferred embodiment. As shown in FIG. 6, the depth D1 of the focal point from the upper surface 11 a in forming the modified layer 23 was set to 500 μm.

Referring to FIG. 8A, there is shown a schematic plan view for illustrating the scanning direction of the laser beam. The separation start point forming step is performed on a forward path X1 and a backward path X2 as shown in FIG. 8A. That is, the modified layer 23 is formed in the hexagonal single crystal ingot 11 on the forward path X1. Thereafter, the focal point of the laser beam is indexed by the predetermined amount. Thereafter, the modified layer 23 is formed again in the ingot 11 on the backward path X2.

Further, in the case that the index amount of the focal point of the laser beam is set in the range of W to 2W where W is the width of the cracks 25 formed on one side of the modified layer 23 along the c-plane 21, the index amount of the focal point is preferably set to W or less until the modified layer 23 is first formed after setting the focal point of the laser beam inside the ingot 11.

For example, in the case that the index amount of the focal point of the laser beam is 400 μm, the index amount is set to 200 μm until the modified layer 23 is first formed inside the ingot 11, and the laser beam is scanned plural times with this index amount of 200 μm as shown in FIG. 8B. That is, a first part of the plural scanning paths of the laser beam is idle, and when it is determined that the modified layer 23 has been first formed inside the ingot 11, the index amount is set to 400 μm and the modified layer 23 is then formed inside the ingot 11.

In this manner, the focal point of the laser beam is sequentially indexed to form a plurality of modified layers 23 at the depth D1 in the whole area of the ingot 11 and also form the cracks 25 extending from each modified layer 23 along the c-plane 21. Thereafter, a wafer separating step is performed in such a manner that an external force is applied to the ingot 11 to thereby separate a plate-shaped member having a thickness corresponding to the thickness of the wafer to be formed from the ingot 11 at the separation start point composed of the modified layers 23 and the cracks 25, thus producing a hexagonal single crystal wafer 27 shown in FIG. 10.

This wafer separating step is performed by using the pressing mechanism 54 shown in FIG. 1. The configuration of the pressing mechanism 54 is shown in FIGS. 9A and 9B. The pressing mechanism 54 includes a head 56 vertically movable by a moving mechanism (not shown) incorporated in the column 52 shown in FIG. 1 and a pressing member 58 rotatable in the direction shown by an arrow R in FIG. 9B with respect to the head 56. As shown in FIG. 9A, the pressing mechanism 54 is relatively positioned above the ingot 11 fixed to the support table 26. Thereafter, as shown in FIG. 9B, the head 56 is lowered until the pressing member 58 comes into pressure contact with the upper surface 11 a of the ingot 11.

In the condition where the pressing member 58 is in pressure contact with the upper surface 11 a of the ingot 11, the pressing member 58 is rotated in the direction of the arrow R to thereby generate a torsional stress in the ingot 11. As a result, the ingot 11 is broken at the separation start point where the modified layers 23 and the cracks 25 are formed. Accordingly, the hexagonal single crystal wafer 27 shown in FIG. 10 can be separated from the hexagonal single crystal ingot 11. After separating the wafer 27 from the ingot 11, the separation surface of the wafer 27 and the separation surface of the ingot 11 are preferably polished to a mirror finish.

There will now be described a wafer producing method according to a preferred embodiment of the present invention with reference to FIGS. 11A to 11C, wherein a plurality of separation start points are formed in the ingot 11. As shown in FIG. 11A, a first separation start point forming step is performed in such a manner that the focal point P of a laser beam LB is set at a first depth (e.g., 1500 μm) three times the depth corresponding to the thickness (i.e., 500 μm) of the wafer from the first surface 11 a of the ingot 11 and the laser beam LB is next applied to the first surface 11 a of the ingot 11 to thereby form a first separation start point 29 a composed of modified layers 23 and cracks 25.

Thereafter, as shown in FIG. 11B, a second separation start point forming step is performed in such a manner that the focal point P of the laser beam LB is set at a second depth (i.e., 1000 μm in this case) obtained by subtracting the depth corresponding to the thickness of the wafer from the first depth of the first separation start point 29 a toward the first surface 11 a of the ingot 11 and the laser beam LB is next applied to the first surface 11 a of the ingot 11 to thereby form a second separation start point 29 b composed of modified layers 23 and cracks 25. Thereafter, as shown in FIG. 11C, a third separation start point forming step is performed in such a manner that the focal point P of the laser beam LB is set at a third depth (i.e., 500 μm in this case) obtained by subtracting the depth corresponding to the thickness of the wafer from the second depth of the second separation start point 29 b toward the first surface 11 a and the laser beam LB is next applied to the first surface 11 a to thereby form a third separation start point 29 c composed of modified layers 23 and cracks 25.

In this manner, the separation start point is stepwise formed inside the ingot 11 as starting from the deepest position toward the first surface 11 a of the ingot 11. Accordingly, the focal point P of the laser beam LB can be set inside the ingot 11 without interfering with the modified layers 23 and the cracks 25 already formed by the laser beam LB. As a result, a plurality of plate-shaped members each having a thickness corresponding to the thickness of the wafer can be separated from the hexagonal single crystal ingot 11 at the plural separation start points, thereby efficiently producing a plurality of wafers each corresponding to the wafer 27 shown in FIG. 10.

The present invention is not limited to the details of the above described preferred embodiment. The scope of the invention is defined by the appended claims and all changes and modifications as fall within the equivalence of the scope of the claims are therefore to be embraced by the invention. 

What is claimed is:
 1. A wafer producing method for producing a hexagonal single crystal wafer from a hexagonal single crystal ingot having a first surface, a second surface opposite to the first surface, a c-axis extending from the first surface to the second surface, and a c-plane perpendicular to the c-axis, the wafer producing method comprising: a separation start point forming step of setting a focal point of a laser beam having a transmission wavelength to the ingot inside the ingot at a predetermined depth from the first surface, which depth corresponds to a thickness of the wafer to be produced, and next applying the laser beam to the first surface as relatively moving the focal point and the ingot to thereby form a modified layer parallel to the first surface and cracks extending from the modified layer along the c-plane, thus forming a separation start point; and a wafer separating step of separating a plate-shaped member having a thickness corresponding to the thickness of the wafer from the ingot at the separation start point after performing the separation start point forming step, thus producing the wafer from ingot; the separation start point forming step including a modified layer forming step of relatively moving the focal point of the laser beam in a first direction perpendicular to a second direction where the c-axis is inclined by an off angle with respect to a normal to the first surface and the off angle is formed between the first surface and the c-plane, thereby linearly forming the modified layer extending in the first direction, and an indexing step of relatively moving the focal point in the second direction to thereby index the focal point by a predetermined amount; the modified layer forming step including a first separation start point forming step of setting the focal point of the laser beam at a first depth which is N times (N is an integer not less than 2) the depth corresponding to the thickness of the wafer from the first surface of the ingot and next applying the laser beam to the first surface of the ingot to thereby form a first separation start point composed of a first modified layer and first cracks extending therefrom, and a second separation start point forming step of setting the focal point of the laser beam at a second depth obtained by subtracting the depth corresponding to the thickness of the wafer from the first depth of the first separation start point toward the first surface of the ingot and next applying the laser beam to the first surface of the ingot to thereby form a second separation start point composed of a second modified layer and second cracks extending therefrom, after performing the first separation start point forming step.
 2. The wafer producing method according to claim 1, wherein the hexagonal single crystal ingot is selected from an SiC single crystal ingot and a GaN single crystal ingot. 